Drying kinetics and energy efficiency of soot ash of smelting silicon manganese alloys under microwave heating

Abstract

Abstract

When smelting silicon manganese alloy in an industrial electric furnace, it will produce smoke and dust waste gas, which can be utilized again back to the furnace and improve the utilization rate of raw materials after a particular trapping device and collection treatment. However, at higher moisture levels, they are prone to explode. Effects of various initial masses, initial moisture contents, and microwave output powers on the soot ash of smelting silicon manganese alloy were studies. The findings indicate that the microwave drying rate increases with all three variables. The time for complete microwave drying is directly proportional to the sample's initial moisture content and the sample's initial mass, and the time for complete microwave drying is inversely proportional to the microwave output power. The results demonstrate that the Modified Page model can accurately describe the microwave drying process. The experimental data were fitted experimentally by drying kinetic models. Microscopic characterization of soot ash from refining silico‑manganese alloys before and after drying was carried out using FTIR and SEM. Through FTIR characterization, the peak value of the -OH absorption peak decreases upon drying, and SEM results in no agglomeration caused by microwave drying and better dispersion of the soot ash of the dried smelted silica‑manganese alloys, all of which proved that microwaves could effectively remove water. It was discovered that the diffusion coefficient increased gradually with increasing power when it was computed using Fick's second law. The diffusion coefficient increases and then decreases as the moisture content increases. The diffusion coefficient decreases as the initial mass increases. Activation energy of microwave drying of soot ash from the refining of silicomanganese alloys was calculated to be −1.4467 W/g. Its purpose is to offer a detailed guide for the industrial drying of soot ash from silicomanganese alloy refinement using microwave drying technology.