Hysteresis-Free Piezoresponse in Thermally Strained Ferroelectric Barium Titanate Films

Abstract

Modern technology asks for thin films of sustainable piezoelectrics, whereas electro-mechanical properties of such films are poorly explored and controlled. Here, dynamic and quasi-static polarization, dielectric, and piezoelectric responses were experimentally studied in thin-film stacks of barium titanate sandwiched between electrodes and grown on top of strontium titanate substrate. Accurate piezoelectric characterization was secured by using double beam interferometric technique. All out-of-plane responses were found to be hysteresis-free. Effective piezoelectric coefficient ~50 pm/V and linear strain-voltage characteristic were achieved. The observed behavior was ascribed to field induced out-of-plane polarization, whereas spontaneous polarization is in-plane due to in-plane tensile thermal strain. Hysteresis-free linear piezoresponse was anticipated in thin films on commercial silicon substrates, enabling large thermal strain.